12cr1mov金相组织/114x10合金钢管高温屈服强度

发布者：无锡市云坤钢管有限公司　　发布时间：2017/2/22　　阅读：1076次

12cr1mov金相组织/114x10合金钢管高温屈服强度

12cr1mov金相组织/114x10合金钢管高温屈服强度规格规格 25×6 83×10-12-14-16-18-20 28×6 89×8-10-12-14-16-18-20 32×6-8 95×6-8-10-12-14-16-20 34×6-8 102×6-7-8-10-12-14-16-20 36×6-8 108×6-7-8-10-12-14-18-20-22 38×6-7-8-9-10 114×6-7-8-10-12-14-18-20 39×8-10 121×6-7-8-10-12-14-16-2…

规格	规格
25×6	83×10-12-14-16-18-20
28×6	89×8-10-12-14-16-18-20
32×6-8	95×6-8-10-12-14-16-20
34×6-8	102×6-7-8-10-12-14-16-20
36×6-8	108×6-7-8-10-12-14-18-20-22
38×6-7-8-9-10	114×6-7-8-10-12-14-18-20
39×8-10	121×6-7-8-10-12-14-16-20
42×6-7-8-9-10	127×-6-7-8-10-12-14-16-20
45×6-7-8-9	133×6-8-12-14-16-18-20-25-30
48×6-7-8-9-10	140×6-7-8-9-10-12-14-16-20-22
51×6-7-8-9-10	146×6-8-12-14-16-18-20-25-30
56×6-7-8-9-10	152×6-8-12-14-16-18-20-25-30
57×6-7-8-9-10-12	159×6-10-12-14
60×6-7-8-9-12-14	159×16-18-20-22-25-30
63×6-7-8-9-10-12-14	168×8-10-12-14-20-25-30-35
68×6-7-8-9-10-12-14-16	180×8-12-16-25-30
70×6-7-8-9-10-12-15-16	180×32-34-38-40
73×6-7-8-9-10-12-15	194×6-8-12-16-20-25-30-40
76×6-7-8-9-10-12-14	203×6-7-10-15-20-25-30

【12cr1mov合金钢管热处理】

淬火加热温度(℃):970;冷却剂:空

回火加热温度(℃):750;冷却剂:空

【12cr1mov合金钢管力学性能】

抗拉强度(σb/MPa):≥490

屈服点(σs/MPa):≥245

断后伸长率(δ5/%):≤22

断面收缩率(ψ/%):≥50

冲击吸收功(Aku2/J):≥71

冲击韧性值αkv (J/cm2):≥88(9)

布氏硬度(HBS100/3000)(退火或高温回火状态):≤179

常温下:许用拉应力(σw/MPa):93 许用弯曲应力(σw/MPa):112 许用剪应力(T/MPa):56

12cr1mov合金钢管主要特性

主要特性:此钢与12CrMoV钢相比，具有更高的抗氧化性及热强性。此钢的蠕变极限与持久强度值很接近，并在持久拉伸的情况下具有高的塑性;钢的工艺性与焊接性良好，但焊前需预热至300℃，焊后需除应力处理。

12cr1mov合金钢管是高压、超高压、亚临界电站锅炉过热器、集箱和主蒸气导管广泛采用的钢种。580℃时仍具有高的热强性和抗氧化性能，有较高的持久塑性。生产工艺较简单，焊接性能良好，但对正火冷却速度较敏感。580℃长期使用会产生珠光体球化。

12cr1mov合金钢管应用举例

这种钢主要在正火及高温回火后使用，用以制造高压设备中工作温度不超过570~585℃的过热钢管、导管、蛇形管及其它相应的锻件。